X52-2 color high chlorinated polyethylene anticorrosive surface coating

Color each color

The composition consists of high chlorinated polyethylene resin, modified resin, plasticizer, pigment, additives, solvents and other components.

Resistant, resistant to oil, heat resistance, low temperature resistance, wear resistance, film toughness, fast drying, low temperature, low temperature, low temperature and low temperature. construction.

Design and use Widely used in metallurgical, petroleum, chemical, construction, energy and other industries chemical pipeline, pipeline, stent, plant and other steel structure equipment and facilities and acid salt salt tank for anti-corrosion, can also be used for concrete structure tower, Cement walls, sewage tanks and other concrete facilities of the anti-corrosion.

Theoretical dosage 180-200 g / m2

 

Wet film thickness of 160 microns

Dry film thickness of 40 microns

Painting method Brush, roll coating, spray

Aging time to open evenly stir to use

Drying time 23 ± 2 ℃: dry 1 hour dry 24 hours after curing 7 days

 

Before the road supporting high chlorinated polyethylene cloud iron anti-rust paint, high chlorinated polyethylene iron red anti-rust paint, high chlorinated polyethylene anti-corrosion intermediate paint.

Diluent High chlorinated polyethylene coating Special diluent dosage 5-10%

Storage period of twelve months