X52-1 high chlorinated polyethylene anticorrosive intermediate paint

Color gray, reddish brown

The composition consists of high chlorinated polyethylene resin, modified resin, mica iron oxide, plasticizer, special pigments, additives, solvents and other components.

Features with excellent moisture resistance, water resistance, chemical resistance and chemical resistance to atmospheric performance, good anti-rust performance. The bottom of the network is good, strong adhesion, dry quickly, a film thickness of 45-50 microns, can reduce the number of construction roads to facilitate the construction.

Designed for use in the chemical atmosphere, industrial atmosphere, acid, alkali, salt corrosion of various types of steel surface corrosion preservative intermediate coating, can also be used in the concrete surface corrosion coating intermediate coating.

Theoretical dosage of 200-250 grams / square meter

 

 

Wet film thickness 170-190 microns

Dry film thickness of 45-45 microns

Aging time to open evenly stir to use

Painting method Brush, roll coating, spray

Drying time 23 ± 2 ℃: dry 1 hour dry 24 hours after curing 7 days

 

Before the road supporting high chlorinated polyethylene cloud iron anti-rust paint, high chlorinated polyethylene iron red anti-rust paint.

After supporting the various colors of high chlorinated polyethylene topcoat

Diluent High chlorinated polyethylene coating Special diluent dosage 10-20%

Storage period of twelve months