H53-4 epoxy cloud iron anti-rust coating (intermediate paint, two-component)

 

Color: reddish brown, gray

 

Composition: Epoxy resin as the base material, mica iron oxide as a pigment and a new anti-rust fillers, anti-rust additives, mixed solvents made of polyamide resin as a curing agent from the preparation of two-component anti-rust coating The

 

Features: The coating is a kind of shielded higher coating, containing high pigment volume concentration of scaly pigments, film after the pigment can be aligned in parallel to the arrangement, similar to the "fish scales" of the lap structure, and therefore has a high closure Sexual, heat resistance and corrosion resistance is good, with a wide range of supporting.

 

Designed for use as an anti-corrosive paint and as a zinc-rich primer coating for increased sealing and corrosion resistance for ships, containers, bridges, gas tanks, port machinery, various steel structures, concrete, etc. The

 

Theoretical dosage: 280 grams / square meter

 

Painting method: brushing, roller coating, spraying

 

Proportion: A component (paint): B component (curing agent) = 6: 1 (weight ratio)

 

Aging time: 23 ± 2 ℃: A and B components after mixing to be cured after 25 minutes to use

 

Applicable period: 23 ± 2 ℃: less than 4 hours

 

Drying time: 23 ± 2 ℃: dry surface ≤ 4 hours hard work ≤ 24 hours fully cured 7 days

 

Painting interval: the shortest 8 hours, the longest limit

 

Painting Road: Recommended 2 Road, dry film thickness of 100 microns.

 

Surface treatment: coated with a primer in the workshop will need two rust, to Sweden derusting standard St3 level; painted in the zinc-rich primer paint, should remove the thin rust, grease, dust and other impurities.

 

Front Road: epoxy zinc-rich workshop primer, epoxy iron red primer, inorganic zinc silicate primer, ethylene phosphating primer