H53-3 epoxy with rust rust primer (two-component)

 

Color: iron red

 

Composition: Epoxy resin, active anti-rust paint, iron oxide red and penetrant, rust additives, mixed solvents, polyamide adducts for the curing agent from the preparation of two-component epoxy anti-rust paint.

 

Features: The coating can produce stable complexes with steel, with excellent water resistance and anti-rust properties, salt spray resistance, resistance to dry and wet performance, resistance to cathodic protection electrode potential performance.

 

Design Uses: Widely used in large-scale steel structure, bridges, steel structure chemical equipment, metallurgy, mining, containers and other anti-corrosion primer.

 

Theoretical dosage: 120-160 g / square

 

Painting method: brushing, roller coating, spraying

 

Proportion: A component (paint): B component (curing agent) = 6: 1 (weight ratio)

 

Aging time: 23 ± 2 ℃: A and B components after mixing to be cured after 25 minutes to use

 

Applicable period: 23 ± 2 ℃: less than 4 hours

 

Drying time: 23 ± 2 ℃: dry surface ≤ 4 hours hard work ≤ 24 hours fully cured 7 days

 

Painting interval: the shortest 24 hours, up to 7 days.

 

Painting Road: Recommended 1, dry film thickness of 30-50 microns.

 

Surface treatment: steel surface should be no oil, floating ash, water rust rust rust, rust layer thickness greater than 60 microns, you should do a simple rust.

 

After the road supporting: epoxy paint, chlorosulfonated polyethylene paint, chlorinated rubber coatings, alkyd paint.

 

Diluent: X-7 epoxy diluent dosage 5-15%

 

Note: 1, the use of the former A and B components must be fully stirred evenly, and then prepared.