H06-2 iron red, zinc yellow, iron black epoxy ester primer

 

Color: iron red, yellow, iron black

 

Composition: from the epoxy ester resin, iron oxide red, zinc oxide and other anti-rust pigments, fillers, driers, anti-rust additives, mixed solvents and other preparation.

 

Features: from dry or low temperature drying, the film tough and durable, good adhesion, if supporting the use of phosphating primer, can improve moisture-proof anti-salt performance.

 

Designed for use in a small number of rust layers or simply rusted steel surfaces. The new rust primer is suitable for corrosion protection on surfaces such as chemical, metallurgical, mining and construction, automotive primer and other steel equipment Painting.

 

Theoretical dosage: 120 g / m2

 

 

Painting method: brushing, roller coating, spraying

 

Proportion: single component, stir evenly to use

 

Painting interval: 23 ± 2 ℃: the shortest 24 hours, the longest limit.

 

Painting Road: Recommended 2, dry film thickness of 80-100 microns.

 

Surface treatment: the surface of the steel components shot blasting or sandblasting treatment, to Sweden derusting standard Sa2.5 level, the formation of steel surface roughness, the general control between 40-80 microns or control the total thickness of the coating in the 1/3 -1 / 2.5 between the rust within 24 hours after painting.

 

Front Road Package: Vinyl Phosphate Primer or Brush Paint

 

After the road supporting: alkyd paint, phenolic resin coating, epoxy finish, chlorinated rubber paint, polyurethane paint, chlorosulfonated and so on.

 

Diluent: X-7 epoxy diluent dosage 5-15%

 

Shelf life: twelve months