S54-31 metal tank anti-corrosion anti-static coating (two-component)

 

Colour: Black

 

Composition: Two-component coatings made from hydroxyacrylic resin, polyisocyanate adduct, conductive pigments, additives, antistatic agents, catalysts, solvents and the like.

 

Features: The paint film resistant to crude oil, 120 # gasoline, 95/130 aviation gasoline, aviation kerosene, 40 # mechanical oil, kerosene, diesel and other petroleum products, and the quality of the oil has no effect (gum ≤ 7mg / 100mg) Paint film with conductive properties, can prevent the oil products in the storage and transportation process due to the accumulation of accidents, use without primer, the paint even coated with 1-2 Road, dry film thickness of 150 microns, so that the film resistance The rate is less than 105Ω, the coating also has excellent corrosion resistance of acid and alkali salt, and coated substrate has an excellent binding force.

 

Design Uses: Suitable for crude oil storage tank, oil and oil storage, oil tanks, oil pipeline wall corrosion protection purposes.

 

Theoretical dosage: 120-150 g / m2

 

Painting method: spray, brush

 

Proportion: Group A: Part B = 4: 1 (by weight)

 

Aging time: After 20 minutes of aging.

 

Applicable period: 23 ± 2 ℃: 4 hours

 

Dry film thickness: 50-80 microns

 

Drying time: 23 ± 2 ℃: Table dry 2 hours 24 hours after curing 12 days

 

Painting Road: Recommended 1-2 Road, dry film thickness of 80-120 microns.

 

Surface treatment: the surface of the steel components shot blasting or sandblasting, to Sweden derusting standard Sa2.5 level, or manual power tool derusting St3 level.

 

Diluent: X-10 Polyurethane coating special diluent dosage 3-5%

 

Storage period: 6 months