J53-13 chlorinated rubber cloud iron antirust paint

 

Color: gray or brown red

 

Composition: from chlorinated rubber, mica iron oxide, plasticizers, additives, solvents and other preparation.

 

Features: Because mica iron oxide is scaly pigment, has a unique shielding performance, pigment composition can be parallel, overlapping arrangement, the shape of "fish scales" general lap structure, so the coating has excellent rust, moisture, chemical resistance performance.

 

Design Uses: Suitable for ships, gas cabinets, marine engineering, petrochemical equipment and other steel structure corrosion, can also be coated with concrete components with a protective layer.

 

Theoretical dosage: 220-240 g / square meter

 

Wet film thickness: 160 microns

 

Dry film thickness: 70 microns

 

Painting method: brushing, roller coating, spraying

 

Aging time: open evenly to stir

 

Drying time: 23 ± 2 ℃: Table dry 2 hours, hard work: 8 hours.

 

Painting interval: 23 ± 2 ℃: the shortest 8 hours, the maximum is not limited

 

Surface treatment: such as direct coating on the steel, the steel required by the second derusting, to the Swedish standard Sa2.5 level, painted in the workshop primer surface is subject to the second derusting, to the Swedish standard St3 level, painting There are chlorinated rubber aluminum powder anti-rust paint, such as has been exposed to long-term exposure to the environment, the application of high pressure fresh water rinse, remove the surface of the oil, the old film, dry and then painted.

 

Before the road supporting: epoxy zinc-rich primer, epoxy derusting primer, epoxy iron red primer, inorganic zinc silicate primer, chlorinated rubber aluminum powder anti-rust paint.

 

After the road supporting: chlorinated rubber anti-rust paint and colored chlorinated rubber finish

 

Painting Road: Recommended 2 Road, dry film thickness of 70-105 microns

 

Diluent: chlorinated rubber coating special diluent dosage 5%

 

Shelf life: twelve months