J52-61 colored chlorosulfonated polyethylene anticorrosive finish

 

Color: colored

 

Composition: from the chlorosulfonated polyethylene rubber as the base material, adding modified resin, rust paint, filler, additives, additives, solvents, curing agent prepared by the two-component coating.

 

Features: Excellent weather resistance, salt resistance, excellent acid resistance, alkali salt corrosion, chemical resistance, water, oil, heat, cold and other properties, excellent physical and mechanical properties, strong adhesion , Strong flexibility, crack resistance, wear, fast drying, low temperature construction.

 

Uses: Widely used in chemical corrosion by the industrial buildings, cement walls, steel structures, chemical pipelines, tanks, equipment and so on. For the acid and alkali storage tank inside and outside the wall, urea, ammonium nitrate granulation tower inside and outside the wall, the workshop warehouse walls, floor and other acid, alkali, salt corrosion equipment or facilities for port terminals, Sewage tanks and other facilities, as well as oil, oil refining and chemical systems construction equipment, tank surface, oil pipeline, oil tanker protective coating.

 

Theoretical dosage: 150-200 g / m2

 

Proportion: bucket stickers

 

Dry film thickness: 15-25 microns

 

Painting method: roller coating, spraying, brushing

 

Drying time: 23 ± 2 ℃: dry for 0.5 hours, dry 24 hours, fully cured 7 days

 

Coating interval: 23 ± 2 ℃: the shortest 2 hours, up to 7 days

 

Qian Road supporting: chlorosulfonated polyethylene preservative primer, chlorosulfonated polyethylene cloud iron intermediate paint

 

Thinner: chlorosulfonated polyethylene paint special thinner

 

Storage period: 6 months