WH61-150 temperature resistant anti-corrosion coating (bottom / topcoat, two-component)

 

Color: Primer: brown, finish: colored

 

Composition: mainly by the epoxy modified silicone resin, special high temperature corrosion resistance pigments, fillers, additives, organic solvents and other components, the bottom paint are A, B two-component packaging.

 

Features: The film has excellent heat resistance, long-term resistance to 150 temperature, with excellent anti-corrosion, chemical resistance of the atmosphere, weather resistance, water resistance, strong adhesion, good flexibility, etc., is cross-linked room temperature from dry Curing paint, drying speed, easy construction.

 

Design Uses: Suitable for high temperature heat, gas pipelines, heating room steel and other temperature at 150 ℃ metal surface of the anti-corrosion coating.

 

Theoretical dosage: primer: 120 g / m2, topcoat: 200 g / m2

 

Painting method: spray, brush, roller coating

 

Proportion: Group A: Part B = 100: 15-16 (weight ratio)

 

Aging time: 23 ± 2 ℃: A and B components after mixing to be cured after 25 minutes to use

 

Applicable period: 25 ± 2 ℃: 6 hours

 

Film thickness: wet film: 80-100 microns, dry film 45-55 microns

 

Drying time: 23 ± 2 ℃: dry 1 hour dry for 24 hours fully cured 7 days

 

Painting interval: the shortest 24 hours, the maximum is not limited.

 

Painting Road: Recommended 2, dry film thickness of 80-100 microns.

 

Surface treatment: the surface of the steel components shot blasting or sandblasting, to Sweden derusting standard Sa2.5 level, or manual power tool derusting St3 level. Steel surface should be rust, degreasing, no dust, no water stains.

 

Diluent: Dedicated diluent dosage 5-15%

 

Shelf life: twelve months