W61-500 high temperature anti-corrosion coating (two-component)

 

Color: Silver

 

Composition: mainly by the silicone resin, special high temperature anti-corrosion pigments, fillers, special additives, organic solvents and other components, for the A, B, C three components packaging.

 

Features: The film has excellent heat resistance, curing speed, long-term resistance to high temperature of 500 ℃, with excellent anti-corrosion, weather resistance, water resistance and construction convenience.

 

Design Uses: Suitable for all kinds of high temperature equipment, such as internal and external coating, such as engines, boilers, exhaust pipes, chimneys, etc., can be used alone or with inorganic zinc silicate primer supporting the use.

 

Theoretical dosage: 120-180 g / m2

 

Painting method: spray, brush, roller coating

 

Proportion: Group A: Component B: Component C = 100: 4: 30 (by weight)

 

Aging time: stir evenly to use

 

Applicable period: 25 ± 2 ℃: 8 hours

 

Wet film thickness: wet film: 60-70 micron dry film: 20-25 microns

 

Drying time: 23 ± 2 ℃: Table dry 2 hours 24 hours after curing 12 days

 

Painting interval: the shortest 24 hours, the maximum is not limited.

 

Painting Road: Recommended 3, dry film thickness of 60-70 microns.

 

Surface treatment: the surface of the steel components shot blasting or sandblasting, to Sweden derusting standard Sa2.5 level, or manual power tool derusting St3 level. Steel surface should be rust, degreasing, no dust, no water stains.

 

Diluent: Dedicated diluent dosage 5-10%

 

Storage period: A component: twelve months, part B: 6 months