X06-1 ethylene phosphating primer (two component)

 

Color: light yellow

 

Composition: from polyvinyl butyral resin, rust paint, phosphoric acid, solvent and other preparation, sub-A, B double cans packaging.

 

Features: In the colored, ferrous metal surface rendering, with strong adhesion, good mechanical strength, fast drying, with paint welding will not affect the welding quality, can be used as workshop primer application, can play rust, phosphating Enhance the adhesion between the substrate and the coating.

 

Uses: mainly as a non-ferrous and black metal surface of the surface treatment agent, can play a role in phosphating, can increase the organic coating and metal surface adhesion, the paint, also known as washing primer, suitable for coating all kinds of piles , Bridges, meters, workshop to Tu, non-ferrous metal backing, ferrous metals and other metal components and equipment surface rust primer.

 

Theoretical dosage: 30-35 g / m2

 

Film thickness: wet film: 15 microns, dry film: 8 microns

 

Proportion: Group A: Part B = 4: 1 (by weight)

 

Ripening time: two components can be used after mixing

 

Applicable period: 23 ± 2 ℃: 8 hours

 

Diluent: do not have to add thinner, such as scrubbing the bottom of the tool, please use X06-1 ethylene phosphating primer special thinner.

 

Painting method: brush, roller coating

 

Drying time: 23 ± 2 ℃: Table dry: 15 minutes, hard work: 2 hours

 

Coating interval: 23 ± 2 ℃: Minimum: 2 hours, the longest: 24 hours

 

Surface treatment: non-ferrous metals to be slightly polished to remove grease; black metal sand blasting rust Sa2.5 level.

 

Painting Road: Recommended brush or roll 1, dry film up to 8 microns

 

After the road supporting: all kinds of anti-rust paint

 

Shelf life: 12 months